Superhydrophobic perfluoropolymer/polystyrene blend films induced by nonsolvent
[ X ]
Tarih
2016
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Science Bv
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Statistical copolymers of perfluoroalkyl ethyl acrylate (Zonyl-TAN) and methyl methacrylate (MMA) were synthesized in a CO2 polymerization system where a CO2-expanded monomer mixture was formed at 13 MPa, and 80 degrees C by using AIBN as initiator. Flat and superhydrophobic surfaces were subsequently prepared on glass slides by applying a phase separation process where the synthesized p(TAN-co-MMA) copolymer and polystyrene (PS) were dissolved in THE solvent. Ethanol was added as the non-solvent to introduce superhydrophobicity during film formation. Water contact angle on the flat p(TAN-co-MMA) copolymer was 118 degrees and increased up to 170 degrees with the formation of surface roughness. The ratio of the ethanol non-solvent in the blend solution has an important effect on the magnitude of surface roughness during the phase separation process. Both pits and protrusions of 1-10 mu m in size were formed on the surface when non-solvent was used. Surface roughness increased with the increase in the ethanol ratio and the PS content of the blend solution. (C) 2016 Elsevier B.V. All rights reserved.
Açıklama
Anahtar Kelimeler
Superhydrophobic surface, Perfluoroalkyl ethyl acrylate, CO2 polymerization, Polystyrene, Phaseseparation, Contact angle
Kaynak
Applied Surface Science
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
383