Non-isothermal degradation kinetics of poly (2,2'-dihydroxybiphenyl)
Yükleniyor...
Tarih
2009
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Catalytic oxidative polymerization of 2,2'-dihydroxybiphenyl (DHBP) was performed by using Schiff base polymer-Cu (II) complex and hydrogen peroxide as catalyst and oxidant, respectively. According to size exclusion chromatography (SEC) analysis, the number-average molecular weight (M (n)), weight-average molecular weight (M (w)) and polydispersity index (PDI) values of poly (2,2'-dihydroxybiphenyl) (PDHBP) were found to be 37,500, 90,000 g mol(-1) and 2.4, respectively. The thermal degradation kinetics was investigated by thermogravimetric analysis in dynamic nitrogen atmosphere at four different heating rates: 5, 10, 15 and 20 A degrees C min(-1). The derivative thermogravimetry curves of PDHBP showed that its thermal degradation process had one weight-loss step. The apparent activation energies of thermal decomposition for PDHBP as determined by Tang, Flynn-Wall-Ozawa (FWO), Kissenger-Akahira-Sunose (KAS), Coats-Redfern (CR) and Invariant kinetic parameter (IKP) methods were 109.1, 109.0, 110.0, 108.4 and 109.8 kJ mol(-1), respectively. The mechanism function and pre-exponential factor were determined by master plots and Criado-Malek-Ortega method. The most likely decomposition process was a D (n) Deceleration type in terms of the CR, master plots and Criado-Malek-Ortega results.
Açıklama
Anahtar Kelimeler
Poly (2,2 '-dihydroxybiphenyl), Kinetic parameter, Mechanism function
Kaynak
Polymer Bulletin
WoS Q Değeri
Q3
Scopus Q Değeri
Q1
Cilt
63
Sayı
2