Polimerik lif katkılı güçlendirilmiş jeopolimer kompozit malzeme üretimi

Basit Öğe Kaydı
dc.contributor.advisorCengiz, Uğur
dc.contributor.authorKartal, Burcu
dc.date.accessioned2025-01-26T20:49:58Z
dc.date.available2025-01-26T20:49:58Z
dc.date.issued2019
dc.departmentÇOMÜ, Enstitüler, Fen Bilimleri Enstitüsü, Enerji Kaynakları ve Yönetimi Ana Bilim Dalı
dc.descriptionFen Bilimleri Enstitüsü, Enerji Kaynakları ve Yönetimi Ana Bilim Dalı
dc.description.abstractBu çalışmada sentetik lif takviyeli jeopolimer betonun yapısal ve malzeme özellikleri araştırılmıştır. Jeopolimerler, normal sıcaklık koşullarında reaktif alümina silikat malzemelerinin ve silikat çözeltilerinin polikondensasyon reaksiyonu ile oluşan kristal olmayan alümina silikat polimerleridir. Mekanizma farklı SiO2, Al2O3, Na2O-K2O ve H2O oranlarından oluşan reaksiyona dayanmaktadır. Lif katkılı jeopolimer malzemelerin kimyasal bileşimlerine bağlı olarak; kanalizasyon boru ürünleri, ateş ve kimyasallara dayanıklı duvar panelleri, koruyucu kaplamalar ve tamir malzemeleri, püskürtme beton ve yüksek performanslı lif katkılı laminatlar gibi çeşitli uygulamalarda kullanılabilmektedir. Bu çalışmada, liflerin metakaolin bazlı jeopolimer betonun mukavemetine etkisine odaklanılmıştır. Lif oranı ağırlıkça % 0-1 arasında tutulmuştur. SiO2/Al2O: 3, Na2O/Al2O: 1, H2O/Na2O: 18 molar oranı sabitlenmiştir. Mekanik karakterizasyon çalışmaları, basınç ve eğilme dayanımı testleri ile gerçekleştirilmiştir. Jeopolimerin yapısal analizleri ve başlangıç materyalleri de XRD, XRF ve FTIR ile araştırılmıştır.
dc.description.abstractIn this study, the structural and material characteristics of synthetic fiber reinforced geopolymer concrete is investigated. Geopolymers are noncrystal alumina silicate polymers formed by the polycondensation reaction of reactive alumina silicate materials and silicate solutions at normal temperature conditions. The mechanism is based on the reaction of different SiO2 - Al2O3 - Na2O or K2O and H2O ratios. Depending on the chemical composition of the fiber reinforced geopolymer materials; source materials and activators can be used in a variety of applications such as sewer piping products, fire and chemical resistant wall panels, wall units, protective coatings and repair materials, shotcrete and high performance fiber reinforced laminates. This study focused on the effect of fibres on mechanical and flexural performance of metakaolin based geopolymer concrete. The fiber ratio was arranged from 0 to 1 % wt. SiO2/Al2O: 3 moles, Na2O /Al2O: 1 mole, H2O/Na2O: 18 moles ratio was fixed. Mechanical characterization studies were carried out by compressive and flexural strength tests. The structure analyses of geopolymer and its starting materials were also investigated by XRD, XRF and FTIR.
dc.identifier.endpage78
dc.identifier.startpage1
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=as2oTjW5jfr9IKSvmCdJYhhhjHZWCo7ohS3RUCjDYrpsO0OYlmrTF7dZkLRv9FEV
dc.identifier.urihttps://hdl.handle.net/20.500.12428/7991
dc.identifier.yoktezid539265
dc.language.isotr
dc.publisherÇanakkale Onsekiz Mart Üniversitesi
dc.relation.publicationcategoryTez
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_Tez_20250125
dc.subjectKimya
dc.subjectChemistry
dc.subjectKimya Mühendisliği
dc.titlePolimerik lif katkılı güçlendirilmiş jeopolimer kompozit malzeme üretimi
dc.title.alternativeProduction of polymeric fiber reinforced geopolymer composite material
dc.typeMaster Thesis

Dosyalar

Koleksiyon

Fen Bilimleri Enstitüsü Tez Koleksiyonu