İmin bağı içeren hidrojellerin sentezi ve karakterizasyonu

Basit Öğe Kaydı
dc.contributor.advisorKaya, İsmet
dc.contributor.authorAyten, Bahar
dc.date.accessioned2025-01-26T20:52:58Z
dc.date.available2025-01-26T20:52:58Z
dc.date.issued2016
dc.departmentÇOMÜ, Enstitüler, Fen Bilimleri Enstitüsü, Kimya Ana Bilim Dalı
dc.descriptionFen Bilimleri Enstitüsü, Kimya Ana Bilim Dalı
dc.description.abstractSunulan tez çalışmasında 2FHK ve 2,7DHN bileşiklerinin asidik çözeltide kitosan template varlığında oksidatif polimerleşmesi ve aynı zamanda kitosanın glutaraldehit ile çapraz bağlanmasıyla oluşan hidrojellerin sentezi ve karakterizasyonu incelendi. Reaksiyon ortamında kitosan template olarak hava ise oksidant olarak kullanıldı. Kitosan template içerisinde polimerleşen dihidroksi polimerleri ile kitosan hidrojen bağı ile çapraz bağlandı. Artan çapraz bağlanma ile viskozitenin arttığı gözlendi. Değişik oranlarda glutaraldehit çapraz bağlayıcısı da kitosan ve glutaraldehit arasında imin bağı oluşturmak için çapraz bağlayıcı olarak kullanıldı. Kitosan hem hidrojen bağı hemde kovalent bağlarla çapraz bağlanarak hidrojel sentezlendi. Sentezlenen hidrojellerin karakterizasyonu FT-IR, TG, SEM, CV analizleri ile yapılmıştır. Sentezlenen tüm hidrojellerin şişme davranışları süreye göre incelendi. Dihidroksi bileşiklerinin asidik kitosan çözeltisi içinde polimerleştiğini karakterize etmek için kitosan NaNO2/HCl kullanılarak depolimerize edildi ve hidroksi polimeri reaksiyon ortamından uzaklaştırıldı. Ayrıca dihidroksi bileşikleri alkali ortamda NaOCl kullanılarak polimerleştirildi ve iki yöntemle elde edilen hidroksi polimerlerinin FT-IR, UV-Vis, 1H NMR ve GPC analizleri yapılarak sonuçlar karşılaştırıldı.
dc.description.abstractIn this study, synthesis and characterization of oxidative polymerization of 2FHK and 2,7DHN compounds in acidic solution with chitosan template and at the same time crosslinking chitosan with glutaraldehyde were studied. Chitosan (CTS) and air were used as template and oxidant, respecticely, in the reaction medium. Dihydroxy polymers were crosslinked with chitosan via hydrogen bond in the reaction medium. The increase of viscosity of reaction medium was observed with increasing crosslinking. Glutaraldehyde (GLA) was used in varying proportions in the reaction medium for forming of C=N (imine) bonding between CTS and GLA. Hydrogel containing both hydrogen and imine bondswas synthesized. Characterizations of synthesized hydrogel were determined by FT-IR, TG, CV, SEM. According to time, swelling ratio of hydrogel was investigated with water. To characterize the polymerized dihydroxide compounds in acidic CTS solution was used NaNO2/HCl for degradation of CTS and precipation of polymer. At the same time, aromatic dihyroxy compound was polymerized by oxidative polycondensation by NaOCl as oxidant in alkaline medium. The polymer obtained via two methods was characterized with FT-IR, UV-Vis, 1H NMR and GPC analysis.
dc.identifier.endpage58
dc.identifier.startpage1
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=DPTyuy3wRPq_qvCPSqUB67wuAbalTENsupRaZd85HMwjpcTF_0u32TQSJODhE3Oc
dc.identifier.urihttps://hdl.handle.net/20.500.12428/8512
dc.identifier.yoktezid457012
dc.language.isotr
dc.publisherÇanakkale Onsekiz Mart Üniversitesi
dc.relation.publicationcategoryTez
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_Tez_20250125
dc.subjectKimya
dc.subjectChemistry
dc.titleİmin bağı içeren hidrojellerin sentezi ve karakterizasyonu
dc.title.alternativeSynthesis and characterization of hydrogels containing imine bonding